ASTM A285 Gr. C Mild Steel Sheet

ASTM 285 Mild Steel Plate Introduction

ASTM A285 is a type of ordinary Carbon Steel intended for fusion-welded pressure vessel equipments as boiler, storage tank, heat exchangers, etc. With 3 steel grades (Grade A, Grade B, Grade C) covering tensile strength range from 310-515Mpa,usually ASTM A285 Steel Plate is delivered as-rolled condition. made by killed, semi-killed, capped or rimmed steel practices according to the end users’ requirement.
ASTM A285 steel could be manufactured into many steel product forms, steel plates, Steel Coil, steel pipe, it has good weld-ability for fusion weld need for pressure vessel equipment, its max thickness is limited to 50mm in order to insure its mechanical property. AGICO ANSON could supply hot rolled and cold rolled ASTM A285 steel plate, customers can also have specific fabrication cutting ( any size and any shape ) drilling, welding, milling, machining and steel structure according to drawing.

Mild Steel Sheet is a type of carbon steel with a low amount of carbon – it is actually also known as “low carbon steel.” Although ranges vary depending on the source, the amount of carbon typically found in mild steel is 0.05% to 0.25% by weight, whereas higher carbon steels are typically described as having a carbon content from 0.30% to 2.0%. If any more carbon than that is added, the steel would be classified as cast iron.

Ms Steel Sheet is not an alloy steel and therefore does not contain large amounts of other elements besides iron; you will not find vast amounts of chromium, molybdenum, or other alloying elements in mild steel. Since its carbon and alloying element content are relatively low, there are several properties it has that differentiate it from higher carbon and alloy steels.

Less carbon means that mild steel is typically more ductile, machinable, and weldable than high carbon and other steels, however, it also means it is nearly impossible to harden and strengthen through heating and quenching. The low carbon content also means it has very little carbon and other alloying elements to block dislocations in its crystal structure, generally resulting in less tensile strength than high carbon and alloy steels. Mild steel also has a high amount iron and ferrite, making it magnetic.

The lack of alloying elements such as those found in stainless steels means that the iron in mild steel is subject to oxidation (rust) if not properly coated. But the negligible amount of alloying elements also helps mild steel to be relatively affordable when compared with other steels. It is the affordability, weldability, and machinability that make it such a popular choice of steel for consumers.